NON ASBESTOS JOINTING SHEETS |
|
FEROLITE NAM 37 GASKET
JOINTING SHEET
|
 |
|
Applications:
|
|
Suitable for water/oil resistant gasket material for
light to medium loading. Suitable for low operating pressure, e.g.
transformers, compressors and apparatus. Also used for easily deformable
components with low surface pressure like valve covers and pans in
internal combustion engines. |
|
Supply Data: |
|
|
|
THICKNESS in mm |
:
|
0.30, 0.50, 0.75, 1.00,1.50,2.00,3.00,4.00 |
|
Sheet Size in mm |
: |
1500X1500, 1500x2000,1500X3000,
1500X4000,1500X4500, 2000x3000 |
|
|
|
Note : Other sheet sizes & thickness upon request |
|
OPERATING CONDITION
|
:
|
Maximum internal pressure: 80
BAR
Maximum Temperature: 220°C
|
|
General data: |
|
|
|
Material Composition (Type of
fibres) |
: |
Made from Aramid Fibre, Mineral Fiber and NBR. |
|
Binders |
: |
NBR |
|
Max.Peak Temp |
: |
300°C |
|
Max. Continuous Temp |
: |
220°C |
|
Max.Continuous Temp.with steam |
: |
160°C |
|
Max. Operating Pressure |
: |
80 bar |
|
Physical Properties: |
|
The following Information Applies to material Thickness 2.0 mm. |
| S.NO. |
PROERTIES |
TEST
METHOD |
UNIT |
SPECIFIED
VALUE |
|
1. |
DENSITY |
---------- |
gm / cm3 |
1.70 - 2.00 |
|
2. |
TENSILE STRENGTH |
|
|
|
|
(a) ACC to ASTM F152(ACROSS GRAIN) |
|
N/mm2 |
> 8 |
|
(b) ACC to DIN52910 (ACROSS GRAIN) |
|
N/mm2 |
> 5 |
|
3. |
COMPRESSIBILITY |
ASTM F36A |
% |
7 – 15 |
|
4. |
RECOVERY |
ASTM F36A |
% |
> 50 |
|
5. |
FLUID ABSORPTION |
|
|
|
|
(a) IN ASTM OIL NO. 3 |
ASTM F 146 |
|
|
|
INCREASE IN MASS |
|
% |
< 15 |
|
INCREASE IN
THICKNESS |
|
% |
< 10 |
|
(b) IN FUEL B |
ASTM F 146 |
|
|
|
INCREASE IN MASS |
|
% |
< 10 |
|
INCREASE IN
THICKNESS |
|
% |
< 10 |
|
(c) IN WATER/ANTIFREEZE |
ASTM F 146 |
|
|
|
INCREASE IN MASS |
|
% |
< 15 |
|
INCREASE IN
THICKNESS |
|
% |
< 7 |
|
6. |
IGNITION LOSS |
DIN 52911 |
% |
< 35 |
|
7. |
SEALABILITY AGAINST NITROGEN |
DIN 3535 |
cm3/min |
< 1.00 |
|
8. |
STRESS RESISTANCE |
|
|
|
|
|
16h 300C |
DIN 52913 |
N/mm2 |
10 |
|
|
16h 175C |
DIN 52913 |
N/mm2 |
~ 28 |
 NOTE:
All data quoted above
are based on years of experience in production & operation of
sealing elements, in view of the wide variety of possible
installation & operating conditions one can not draw final
conclusion in all application cases regarding the behavior in gasket
joint. The data may not therefore, be used to support any warranty
claims.