NON ASBESTOS JOINTING SHEETS |
|
FEROLITE NAM 32 GASKET
JOINTING SHEET
|
 |
|
Applications:
|
|
Suitable
for high performance, oil resistant gasket material with
excellent thermal, chemical & mechanical properties. Suitable
for compressors, pipelines, apparatus, transmission, gas meters
and internal combustion engines, pipe unions & pumps etc. |
|
Supply Data: |
|
|
|
THICKNESS in mm |
:
|
0.30,
0.50, 0.75, 1.00,1.50,2.00,3.00,4.00 |
|
Sheet Size in mm |
: |
1500X1500, 1500x2000,1500X3000, 1500X4000, 1500X4500, 2000x3000. |
|
|
|
Note : Other sheet sizes & thickness upon request |
|
OPERATING CONDITION
|
:
|
Maximum internal pressure: 150
BAR
Maximum Temperature:
270°C
|
|
General data: |
|
|
|
Material Composition (Type of
fibres) |
: |
Aramid Fiber, Mineral Fibre. |
|
Binders |
: |
NBR |
|
Max.Peak Temp |
: |
400°C |
|
Max. Continuous Temp |
: |
270°C |
|
Max.Continuous Temp.with steam |
: |
240°C |
|
Max. Operating Pressure |
: |
150 bar |
|
Physical Properties: |
|
The following Information Applies to material Thickness 2.0 mm. |
| S.NO. |
PROERTIES |
TEST
METHOD |
UNIT |
SPECIFIED
VALUE |
|
1. |
DENSITY |
---------- |
gm / cm3 |
1.70 - 2.00 |
|
2. |
TENSILE STRENGTH |
|
|
|
|
(a) ACC to ASTM F152(ACROSS GRAIN) |
|
N/mm2 |
> 14 |
|
(b) ACC to DIN52910 (ACROSS GRAIN) |
|
N/mm2 |
> 11 |
|
3. |
COMPRESSIBILITY |
ASTM F36A |
% |
6 – 12 |
|
4. |
RECOVERY |
ASTM F36A |
% |
> 50 |
|
5. |
FLUID ABSORPTION |
|
|
|
|
(a) IN ASTM OIL NO. 3 |
ASTM F 146 |
|
|
|
INCREASE IN MASS |
|
% |
< 10 |
|
INCREASE IN
THICKNESS |
|
% |
< 8 |
|
(b) IN FUEL B |
ASTM F 146 |
|
|
|
INCREASE IN MASS |
|
% |
< 10 |
|
INCREASE IN
THICKNESS |
|
% |
< 7 |
|
(c) IN WATER/ANTIFREEZE |
ASTM F 146 |
|
|
|
INCREASE IN MASS |
|
% |
< 15 |
|
INCREASE IN
THICKNESS |
|
% |
< 7 |
|
6. |
IGNITION LOSS |
DIN 52911 |
% |
< 30 |
|
7. |
SEALABILITY AGAINST |
DIN 3535 |
cm3/min. |
< 0.5 |
|
8. |
STRESS RESISTANCE |
|
|
|
|
|
16h 300C |
DIN 52913 |
N/mm2 |
~ 25 |
|
|
16h 175C |
DIN52913 |
N/mm2 |
~ 30 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
 NOTE:
All data quoted above
are based on years of experience in production & operation of
sealing elements, in view of the wide variety of possible
installation & operating conditions one can not draw final
conclusion in all application cases regarding the behavior in gasket
joint. The data may not therefore, be used to support any warranty
claims.
Should you have any doubts about the
choice of gasket material, please refer to us. Our engineering cell
will be happy to assist you.
|