ASBESTOS JOINTING SHEETS |
|
FEROLITE 'CS' GASKET
JOINTING SHEET
|
 |
|
Applications: |
|
Suitable for Controlled swelling in oil medium
stress condition & is suitable for Internal Combustion engines
as well as in Compressors pipe system.
|
| Supply Data: |
|
|
|
THICKNESS in mm |
:
|
0.30, 0.50, 0.75, 1.00, 1.50, 2.00, 3.00, 4.00. |
| Sheet Size in mm |
: |
1500X1500, 1500x2000,1500X3000, 1500X4000, 1500X4500, 2000x3000. |
|
|
Note : Other sheet sizes & thickness upon request |
| General data: |
|
|
|
Material Composition (Type of
fibres) |
: |
Chrysotile Asbestos Fiber |
| Material Type |
: |
Compressed Fiber Jointings --Calendared |
| Binders |
: |
Synthetic & Natural Elastomers |
| Surface Finish |
: |
Yellow |
| Specification Compliance |
: |
ISI: 2712/1998 Grade O/1,W/1 |
|
|
ASTM: F 104 F112950 M 7 |
| Max.Peak Temp |
: |
500°C |
| Max. Operating Pressure |
: |
100 bar |
| Physical Properties: |
|
The following Information Applies to material Thickness 1.5 mm. |
| S.NO. |
PROERTIES |
TEST
METHOD |
UNIT |
SPECIFIED
VALUE |
| 1. |
DENSITY |
ASTM F104 |
gm / cm3 |
1.70 - 2.20 |
| 2. |
TENSILE STRENGTH |
ASTM F104 |
Mpa |
> 26 |
| 3. |
COMPRESSIBILITY |
ASTM F104 |
% |
6 – 14 |
| 4. |
RECOVERY |
ASTM F104 |
% |
> 40 |
| 5. |
IGNITION LOSS |
ASTM F104 |
% |
< 28 |
| 6. |
STRESS RESISTANCE |
ASTM F104 |
Mpa |
> 23 |
| 7. |
FLUID ABSORPTION |
|
|
|
|
|
IN ASTM OIL NO.3 |
|
|
|
|
|
(a) Thickness Increase |
ASTM F104 |
% |
20 - 40 |
|
|
(b) Mass Increase |
ASTM F104 |
% |
15 - 30 |
|
|
IN FUEL B |
|
|
|
|
|
(a) Thickness Increase |
ASTM F104 |
% |
20 - 40 |
|
|
(b) Mass Increase |
ASTM F104 |
% |
10 - 20 |
|
|
IN WATER |
|
|
|
|
|
(a) Mass Increase |
ASTM F104 |
% |
< 10 |
NOTE:
All data quoted above
are based on years of experience in production & operation of
sealing elements, in view of the wide variety of possible
installation & operating conditions one can not draw final
conclusion in all application cases regarding the behavior in gasket
joint. The data may not therefore, be used to support any warranty
claims.
Should you have any doubts about the
choice of gasket material, please refer to us. Our engineering cell
will be happy to assist you. |